Product Details:
|
Material: | Silicon Carbide (SiC),SSiC Or SiSiC,silicon Carbide Ceramic,high Sic | Application: | Industrial Ceramic,Refractory,Industrial Furnaces,Structure Ceramic,Wear Resistant Industry |
---|---|---|---|
Shape: | Pipe,Customized | Type: | Ceramic Tubes |
Raw Material: | Silicon Carbide Powder,Imported From Saint-Gobain,High Purity Silicon Nitride,Silicon Carbide(SiC) | Size: | 1/4 To 4 Inch,Size Customized,Customers' Requests,230*114*65/75 |
Working Temperature: | 1380℃ | Usage: | Semiconductor,Wear-resisting Material,High Temperature And Anti- Acid,Kiln |
High Light: | silicon carbide rollers,silicon carbide pipe |
Reaction Sintered Silicon Carbide Sisic Roller Usage Lithium Battery Production Site
In the production process of ceramic furnace roller, molding process is one of the key parts.
At present, ceramic roller production mainly uses three molding methods: grouting, isostatic pressing and extrusion molding.
In grouting process, the ceramic powder is formulated into a fluid slurry, and then injected into a porous mold.
Moisture is absorbed into the mold to form a uniform layer of mud with a certain thickness. At the same time,
a certain strength is formed in the dehydration process. Physically grouting has high requirements on mud
performance, and grouting requires a huge production site, resulting in poor product density, high labor intensity,
and low production efficiency. Currently the application is small and has been replaced by plastic extrusion.
Isostatic pressing, also known as hydrostatic pressure molding, is a molding method that utilizes the incompressibility
of a liquid medium and the uniform transmission of pressure. In the process, the material will be firstly formed into a
tubular shape on a roller blank forming mold, and then a layer of skin jacket is sheathed on the surface of the blank
and placed in a hydraulic press. Pressure is transmitted to the bladder through the liquid, and then the pressure is
removed from the hydraulic press, and the blank can be sent for kiln firing. The water content of the isostatic pressing
roller blank is about 1%, and the forming pressure can be between 80-150 MPa, depending on the blank composition
and the diameter and length of the roller blank. The advantage of isostatic pressing is that there is no dry and deform
of the blanks, and the strength of the blank is large.
The disadvantage is that the equipment investment is large and the production process is complicated.
Plastic extrusion molding is the use of peat has a plasticity characteristics, after a certain process processing
made of a certain shape of the body. The process of this method is as follows: the billet is ball-milled, sifted,
dehydrated into mudcake by high-pressure mud pump and high-pressure filter press, or evenly blanked by
pretreated raw material and water mixing station. The vacuum mud mixer mixes the ingredients and moisture
of the blank even more and degassing. There are two types of plastic forming machines, one is a piston type
hydraulic extruder, and the other type is a vacuum spiral extrusion molding machine.
Silicon Carbide Product Specification: | ||||
Item | Unit | SSIC | RBSIC SISIC | R-SIC |
Purity | ( % ) | ≥ 99 | ≥90% | ≥ 99 |
Application temperature | ºC | 1700 | 1380 | 1650 |
Density | g/CM2 | ≥3.10-3.15 | ≥3.02 | 2.65-2.75 |
Open porosity | % | ≤0.1 | ≤0.1 | |
Hardness | ≥92 HRA | 2400 Kg/mm2 | 1800-2000 Kg/mm2 | |
Bending strength | MPa | 400-580 | 250(20ºC) | ≥300 |
281(1200ºC) | ||||
Tensile strength | Mpa | ≥200 | ≥190 | |
modulus of elasticity | GPa | 400 | 332(20ºC) | 80-100(20ºC) |
300(1200ºC) | 90-110(1200ºC) | |||
Thermal Conductivity | W/m.k | 100-120 | 45(1200ºC) | 36 |
Coefficient of thermal expansion | K1X 106 | 4.2 | 4.5 | 4.6 |
Rigidity | Gpa | >25 | 13 | |
Acid&Ikali resistance | Excellent | Excellent | Excellent |
SiC Product Specification: | ||||
Item | Unit | OC-1 | OC-2 | MC-3 |
SiC | (%) | ≥90 | ≥86 | ≥80 |
Apparent Porosity | (%) | ≤10 | ≤13 | ≤16 |
Density | g/CM2 | ≥2.66 | ≥2.63 | ≥2.6 |
Application temperature | ºC | ≥1680 | ≥1620 | ≥1550 |
Coefficient of thermal expansion | aX 10-6/ºC | ≤4.8 | ≤5.0 | ≤5.5 |
Bending Strength | 1200ºC | ≥45 | ≥40 | ≥30 |
FAQ:
Q: Are you trading company or manufacturer ?
A:We are professional Sisic manufacturer.
Q: How long is your delivery time?
A: Generally it is 5-10 days if the goods are in stock. or it is 30-35 days if the goods need production, according to quantity.
Q: Do you provide samples ? is it free or extra ?
A: Yes, we could offer the sample for free charge but do not pay the cost of freight.
Q: What is your terms of payment ?
A: Payment<=1000USD, 100% in advance. Payment>=1000USD, 30% T/T in advance ,balance against the finished bulk goods.
If you have another question, pls feel free to contact us as below:
Contact Person: Ms. Alice Zhang
Tel: +86-15095283678
Fax: 86-536-2667818