Product Details:
|
| Material: | Silicon Carbide (SiC) | Application: | Industrial Ceramic |
|---|---|---|---|
| Sic Content (%): | 85%Min | Density: | ≥3.02g/cm3 |
| Raw Material: | Silicon Carbide Powder | Thermal Conductivity: | 45W/m.k(1200℃) |
| Size: | Size Customized | Working Temperature: | 1380℃ |
| Product Name: | Reaction Bonded Silicon Carbide Ceramic Beam | Bulk Density: | Min 3.02g/cm3 |
| High Light: | refractory kiln furniture,ceramic beam |
||
SISIC silicon carbide procelain cross beam manufacturer used to tunnel kiln
High temperature creep resistant Refractory silicone carbide Beam(Sisic Beam)
The recrystallized ceramic beam we produced is made by alpha silicon carbide powder,sintered under 2400 celsius after molding,
the SIC purity is more than 99%,no other combining phase,with high strength under high temperature,the recrystallized ceramic
beam is suitable for shuttle kiln.Our company have accumulated and summarized much recrystallized ceramic beam application
experience according to continue research for many years,of course there are still many problems need us to explore.In a word,
the practice application of recrystallized ceramic beams still need continuous research,in order to get scientific and proper
application in the sintering process of the ceiling kiln and shuttle kiln,to make the producers and users of the recrystallized silicon
carbide beams reach a consensus and promote scientific and technological progress.
Characteristics of recrystallized silicon carbide ceramic beam:(Sisic Beam)
1.Recrystallized silicon carbide ceramic beam with high temperature resistance,it can keep natural temperature strength under
high temperature,even slightly elevated.The bending strength is 80～100MPa under 20℃,and 90～110MPa under 1400℃,that’s
the experiment test data,so this kind of material is more suitable for high temperature bearing parts.
2.Corrosion resistance,in the acidic medium,even in high temperature acidic environment,such as boiling HCl,H2SO4,HNO3,
liquated KClO3,KNO3,it can both bearing and no reaction.
3.Good thermal conductivity,the thermal conductivity of recrystallized ceramic beam is 28W/m·K,better than alumina, oxide
bonded silicon carbide,forsterite porcelain,mullite etc.So for recrystallized ceramic beam,good thermal conductivity can reduce
thermal shock and improve thermal shock resistance.
4.Recrystallized ceramic beam has low coefficient of thermal expansion,with an average of 4．8×10－6 /℃,lower than alumina
porcelain,electrical porcelain,magnesia porcelain etc.
5.Good oxidation resistance,and more oxidation resistance than other non-oxide ceramics.When the component beam is using
under high temperature,the surface silicon carbide is oxidized to form a SiO2 film,the film is delayed and reduced the oxidation rate.
| SISIC Technical Date | ||
| Item | Unit | Data |
| Max temperature of application | ºC | 1380 |
| Density | g/cm3 | ≥3.02 |
| Open porosity | % | <0.1 |
| Bending strength | Mpa | 250(20ºC) |
| Mpa | 280(1200ºC) | |
| Modulus of elasticity | Gpa | 330(20ºC) |
| Gpa | 300(1200ºC) | |
| Thermal conductivity | W/m.k | 45(1200ºC) |
| Coefficient of thermal expansion | K-1×10-6 | 4.5 |
| Rigidity | 13 | |
| Acid alkaline-proof | Excellent | |
Photos of reference
Yui
WEIFANG BETTER CERAMIC CO., LTD
MOB:+86-18615910108(Whatsapp)
TEI:+86-536-2693828
Wechat:18615910108 QQ:3001737400
Email:yui@wf-better.com Web:www.wf-better.com
Hot tag:ceramics square beam,supplier,factory,manufactures,good price,bearing structure beam,kiln furance